Leccion1.Introduccion.Datos

VIDRIOS
LOS VIDRIOS FORMAN UN GRUPO FAMILIAR DE
CERÁMICAS
LA NOBLEZA DEL VIDRIO RESIDE EN UN CONJUNTO DE CUALIDADES
QUE SON:
- TRANSPARENCIA ÓPTICA
- RESISTENCIA ESTRUCTURAL (Material elástico)
Rc=1000 Mpa, Rf=40 Mpa (Pulido recocido),
Rf=120-200 MPa (Templado)
Módulo de elasticidad (Vidrio común): E = 70 Gpa
- AISLAMIENTO TERMICO Y ACUSTICO
(CONFORT EN EL HABITAT)
-LA FACILIDAD CON QUE PUEDE FABRICARSE
(DIFERENTES FORMAS Y COLORES)
LO EMPLEAMOS SIN MAYOR PROBLEMA, SABIENDO QUE
CON UN GOLPE NO MUY FUERTE SE PUEDE ROMPER
(FRAGILIDAD).
EN LA ACTUALIDAD EXISTEN CRISTALES DE 6 mm DE ESPESOR,
TOTALMENTE INCOLOROS, QUE PERMITEN FILTRAR HASTA EL 70 %
DE LA RADIACIÓN INFRARROJA Y EL 99.5% DE LA ULTRAVIOLETA
O CRISTALES DE 12 mm. QUE DETIENEN UN PROYECTIL
CALIBRE 9 mm
PARA RESPONDER A LAS EXIGENCIAS DE LOS USUARIOS, LOS
VIDRIOS DEBEN CUMPLIR UNA SERIE DE FUNCIONES, COMO SON:
A. CONTROL DE TRANSMISIÓN DE LUZ.
B. CONTROL DE TRANSMISIONES NO DESEADAS (ENERGÍA, RUIDO,
RADIACIÓN ULTRAVIOLETA, ETC.)
C. PROTECCIÓN DE LAS PERSONAS Y BIENES
D. FUNCIÓN DE SOPORTE DE COMUNICACIÓN ENTRE EL INTERIOR Y
EL EXTERIOR.
E. ARMONIZAR EL ASPECTO ESTÉTICO.
PARA SATISFACER ESTAS NECESIDADES SE REALIZAN NUMEROSOS
PROCESOS DE TRANSFORMACIÓN DEL VIDRIO
ACTUALMENTE, MEDIANTE LA
COMBINACIÓN DE VARIOS TIPOS DE VIDRIOS, SE PUEDEN
CONSEGUIR LA MAYORÍA DE LAS FUNCIONES EXIGIDAS.
EL VIDRIO ES UN MATERIAL SANO Y PURO. POR ELLO, CONSTITUYE
UN ENVASE IDEAL PARA LOS PRODUCTOS ALIMENTICIOS QUE
PUEDEN SER CONSERVADOS DURANTE LARGOS PERIODOS DE
TIEMPO SIN ALTERACIÓN DE SU GUSTO NI DE SUS AROMAS.
EL VIDRIO OFRECE TAMBIÉN MÚLTIPLES POSIBILIDADES DE
FORMAS, COLORES Y PUEDE DECORARSE POR MEDIO DE VARIAS
TÉCNICAS. LA BOTELLA O EL TARRO PUEDEN POR LO TANTO SER
PERSONALIZADOS EN FUNCIÓN DE SU CONTENIDO.
Puede presentarse con diferentes formas y procesos de fabricación:
- V. PLANO
- V. HUECO
- V. MOLDEADO
- V. en TUBOS
- V. en FIBRAS
- V. de OPTICA
- V. ARTISTICO
- V. ESPECIALES
MISIONES
FUNCIONES DEL VIDRIO
ESTETICA y
DISEÑO
- TRANSPARENCIA
- COLOR
- DIMENSIONES / FORMAS
- AISLAMIENTO TERMICO
CONFORT
- AISLAMIENTO ACUSTICO
- TRANSMISION OPTICA / CALIDAD
- RESISTENCIA MECANICA
SEGURIDAD
- PROTECCION BIENES / PERSONAS
- DURABILIDAD
EXIGENCIAS PARA EL VIDRIO PLANO
COMO MATERIAL DE CONSTRUCCIÓN.
LA PRODUCCIÓN MUNDIAL DE VIDRIO PLANO FUE DE ≈ 44x106 t
AÑO
2006
The global market for flat glass in 2004 was approximately 38 million
tonnes. (1 tonelada ~ 125 m2 → 4750 millones de m2) At the level of
primary manufacture this represents a value of around EUR 15 billion.
Of this tonnage, around 70 per cent is consumed in windows for
buildings, 10 per cent in glazing products for automotive applications
and 20 per cent used in furniture (mobiliario, lámparas y accesorios)
and other interior applications.
Of this demand, around 23 million tonnes is high quality float glass.
Around 3 million tonnes is satisfied by sheet glass production (a
process where molten glass is drawn out of the furnace vertically and
subjected to an inferior annealing process)
and 2 million tonnes is rolled glass (a process where molten glass is
squeezed between rollers to form sheets, usually with a pattern
embossed (estampado) on the surface). The remaining 10 million
tonnes is lower quality float, produced mainly in China.
A proportion of the high quality float glass, and indeed some of
the rolled, is further processed by laminating, toughening,
coating and silvering, for use typically in insulating glass units
or automotive glazings. At this level the market has a value of
approximately EUR 44 billion.
Europe, China and North America together account for 75 per cent of
global demand for glass. Europe is the most mature glass market
and has the highest proportion of value-added products
Just four companies; Pilkington, Saint-Gobain, Asahi and Guardian,
produce 61 per cent of the world's high quality float glass. Much of
the world’s lower quality float and sheet glass production is being
replaced by high quality float
There are only three glass groups with global automotive glazing
capability and presence. Pilkington, Asahi and Saint-Gobain,
together with their respective associates and strategic partners,
supply 76 per cent of the world's Original Equipment (OE) glazing
requirements.
Año 2002
Año 2004
LA PRODUCCIÓN ESPAÑOLA DE LUNA FLOTADA ES DE, ALREDEDOR,
DEL MILLÓN DE TONELADAS, ESTANDO SITUADAS LAS FÁBRICAS EN:
AVILÉS (ASTURIAS)(FIGURA), ARBÓS (TARRAGONA) QUE PERTENECEN
A SAINT GOBAIN, TUDELA (NAVARRA) (219000 t/año), LLODIO (ALAVA),
QUE PERTENECEN A GUARDIAN Y SAGUNTO (VALENCIA), QUE
PERTENECE A PILKINGTON/ASAHI (150000 t/año)
La Federación Europea del Envase de Vidrio FEVE- ha dado a
conocer los resultados del reciclado integral de envases de
vidrio en 2003, que ha permitido que las industrias vidrieras
europeas hayan introducido en sus hornos 30.051,4 millones
de envases de vidrio para fabricar nuevas botellas y tarros.
La cantidad de botellas y tarros incorporados a los hornos
vidrieros durante el 2003 supone un incremento de 1.390,5
unidades sobre 2001. La aportación media de cada
ciudadano europeo de los 17 países integrados en la FEVE se
situó en 67 botellas y tarros, tres envases más que en 2002.
Nuevamente Alemania es el país en el que se ha reciclado un
número mayor de botellas y tarros, pero sin embargo es
Suiza con 134 envases- el que lidera el ranking en cuanto
aportación envase/habitante. Tras los suizos están los
franceses con una media de participación de 109 botellas y
tarros por habitante.
Hitos más destacables de la historia del vidrio.